Minimal Match — 49.1% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS403 (JIS G4304:2021) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS403 is typically used for hot-rolled stainless steel plates and strips, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners..
JIS G4304 SUS403 is defined under Japanese Industrial Standards (JIS), originating from Japan, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.
As per chemical composition, JIS G4304 SUS403 vs GB/T 3280 06Cr19Ni10 is a 73.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 49.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS403
GB/T 3280 06Cr19Ni10
Tensile Strength
>=440 MPa
520-720 MPa
Yield Strength
>=205 MPa
205-310 MPa
Elongation
>=20%
40-60%
Hardness
<=201 HB
187 HB max
Condition
Annealed plate and strip; proof strength applies only when specified by the purchaser
Not specified
Typical Applications
JIS G4304 SUS403
Hot-rolled stainless steel plates and strips
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Can JIS G4304 SUS403 Be Substituted With GB/T 3280 06Cr19Ni10?
JIS G4304 SUS403 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between JIS G4304 SUS403 and GB/T 3280 06Cr19Ni10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS403 be substituted with GB/T 3280 06Cr19Ni10?
JIS G4304 SUS403 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.