Minimal Match — 45.2% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS410L (JIS G4304:2021) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS410L is typically used for hot-rolled stainless steel plates and strips, while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware.
JIS G4304 SUS410L is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.
As per chemical composition, JIS G4304 SUS410L vs EN 10088-1 1.4301 is a 67.8% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 45.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS410L
EN 10088-1 1.4301
Tensile Strength
>=360 MPa
≥520 MPa
Yield Strength
>=195 MPa
≥210 MPa
Elongation
>=22%
≥45%
Hardness
<=183 HB
≤215 HB
Condition
Annealed plate and strip; proof strength applies only when specified by the purchaser
Not specified
Typical Applications
JIS G4304 SUS410L
Hot-rolled stainless steel plates and strips
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Can JIS G4304 SUS410L Be Substituted With EN 10088-1 1.4301?
JIS G4304 SUS410L and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between JIS G4304 SUS410L and EN 10088-1 1.4301?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS410L be substituted with EN 10088-1 1.4301?
JIS G4304 SUS410L and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.