Strong Match — 100% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS430LX (JIS G4304:2021) and JIS G4305 SUS430LX (JIS G4305:2012) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS430LX is typically used for hot-rolled stainless steel plates and strips, while JIS G4305 SUS430LX is commonly used for cold-rolled stainless steel plates, sheet and strip.
JIS G4304 SUS430LX is defined under Japanese Industrial Standards (JIS), originating from Japan, while JIS G4305 SUS430LX is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, JIS G4304 SUS430LX vs JIS G4305 SUS430LX is a 100% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 100%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS430LX
JIS G4305 SUS430LX
Tensile Strength
>=360 MPa
>=360 MPa
Yield Strength
>=175 MPa
>=175 MPa
Elongation
>=22%
>=22%
Hardness
<=183 HB
<=183 HB
Condition
Annealed plate and strip; proof strength applies only when specified by the purchaser
Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
JIS G4304 SUS430LX
Hot-rolled stainless steel plates and strips
JIS G4305 SUS430LX
Cold-rolled stainless steel plates, sheet and strip
Can JIS G4304 SUS430LX Be Substituted With JIS G4305 SUS430LX?
JIS G4304 SUS430LX and JIS G4305 SUS430LX overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS430LX is often considered as a substitute for JIS G4304 SUS430LX in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G4304 SUS430LX and JIS G4305 SUS430LX?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS430LX be substituted with JIS G4305 SUS430LX?
JIS G4304 SUS430LX and JIS G4305 SUS430LX overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS430LX is often considered as a substitute for JIS G4304 SUS430LX in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.