JIS G4304 SUS434 vs ASTM A959 316Cb

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS434 (JIS G4304:2021) and ASTM A959 316Cb (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS434 is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 316Cb is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS434 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 316Cb is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS434 vs ASTM A959 316Cb is a 74.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With JIS G4304 SUS434:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
74.7%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property JIS G4304 SUS434 ASTM A959 316Cb
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.08
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=2.00
P (%) <=0.040 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.00-18.00 16.0-18.0
Mo (%) 0.75-1.25 2.00-3.00
Ni (%) <=0.60 10.0-14.0
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS434 ASTM A959 316Cb
Tensile Strength >=450 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=22% Not specified
Hardness <=183 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS434
Hot-rolled stainless steel plates and strips
ASTM A959 316Cb
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4304 SUS434 Be Substituted With ASTM A959 316Cb?
JIS G4304 SUS434 and ASTM A959 316Cb share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4304 SUS434
0 active listings and RFQs →
ASTM A959 316Cb
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS434 and ASTM A959 316Cb?
ASTM A959 316Cb specifies N which is not specified for JIS G4304 SUS434.
Can JIS G4304 SUS434 be substituted with ASTM A959 316Cb?
JIS G4304 SUS434 and ASTM A959 316Cb share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.