Close Alternative — 74% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS434 (JIS G4304:2021) and EN 10088-1 X6CrMoS19-2 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS434 is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X6CrMoS19-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4304 SUS434 vs EN 10088-1 X6CrMoS19-2 is a 74% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 74%.

Frequently Compared With JIS G4304 SUS434:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
74%
MECHANICAL MATCH
No shared data
OVERALL
74%
Specifications
Property JIS G4304 SUS434 EN 10088-1 X6CrMoS19-2
Standard JIS G4304:2021 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.080
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=2.50
P (%) <=0.040 <=0.040
S (%) <=0.030 0.15-0.35
Cr (%) 16.00-18.00 17.5-19.5
Mo (%) 0.75-1.25 1.50-2.50
Ni (%) <=0.60 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS434 EN 10088-1 X6CrMoS19-2
Tensile Strength >=450 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=22% Not specified
Hardness <=183 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS434
Hot-rolled stainless steel plates and strips
EN 10088-1 X6CrMoS19-2
Not documented
Can JIS G4304 SUS434 Be Substituted With EN 10088-1 X6CrMoS19-2?
JIS G4304 SUS434 and EN 10088-1 X6CrMoS19-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4304 SUS434
0 active listings and RFQs →
EN 10088-1 X6CrMoS19-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS434 and EN 10088-1 X6CrMoS19-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS434 be substituted with EN 10088-1 X6CrMoS19-2?
JIS G4304 SUS434 and EN 10088-1 X6CrMoS19-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.