Related Material — 69.9% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS436J1L (JIS G4304:2021) and ASTM A959 S18235 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS436J1L is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 S18235 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS436J1L is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 S18235 is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS436J1L vs ASTM A959 S18235 is a 75.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With JIS G4304 SUS436J1L:
EN 10088-1 1.4006 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
75.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property JIS G4304 SUS436J1L ASTM A959 S18235
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.025 <=0.025
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=0.50
P (%) <=0.040 <=0.040
S (%) <=0.030 0.15-0.35
Cr (%) 17.00-20.00 17.5-18.5
Mo (%) 0.40-0.80 2.00-2.50
N (%) <=0.025 <=0.025
Ni (%) <=0.60 <=1.00
Ti (%) <=0.80 0.030-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS436J1L ASTM A959 S18235
Tensile Strength >=410 MPa Not specified
Yield Strength >=245 MPa Not specified
Elongation >=20% Not specified
Hardness <=192 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS436J1L
Hot-rolled stainless steel plates and strips
ASTM A959 S18235
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can JIS G4304 SUS436J1L Be Substituted With ASTM A959 S18235?
JIS G4304 SUS436J1L and ASTM A959 S18235 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4304 SUS436J1L
0 active listings and RFQs →
ASTM A959 S18235
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS436J1L and ASTM A959 S18235?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS436J1L be substituted with ASTM A959 S18235?
JIS G4304 SUS436J1L and ASTM A959 S18235 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.