JIS G4304 SUS630 vs GB/T 3280 06Cr19Ni10

Minimal Match — 47.2% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS630 (JIS G4304:2021) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS630 is typically used for hot-rolled stainless steel plates and strips, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. JIS G4304 SUS630 is defined under Japanese Industrial Standards (JIS), originating from Japan, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, JIS G4304 SUS630 vs GB/T 3280 06Cr19Ni10 is a 70.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 47.2%.

Frequently Compared With JIS G4304 SUS630:
ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4845 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
70.9%
MECHANICAL MATCH
0%
OVERALL
47.2%
Specifications
Property JIS G4304 SUS630 GB/T 3280 06Cr19Ni10
Standard JIS G4304:2021 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.07 0.08 max
Si (%) <=1.00 1.00 max
Mn (%) <=1.00 2.00 max
P (%) <=0.040 0.045 max
S (%) <=0.030 0.030 max
Ni (%) 3.00-5.00 8.00-11.00
Cr (%) 15.00-17.50 18.00-20.00
Cu (%) 3.00-5.00 Not specified
Nb (%) 0.15-0.45 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS630 GB/T 3280 06Cr19Ni10
Hardness <=363 HB 187 HB max
Condition Solution heat treated plate and strip (no strength values specified; aged conditions are in the blocks) Not specified
Tensile Strength Not specified 520-720 MPa
Yield Strength Not specified 205-310 MPa
Elongation Not specified 40-60%
Typical Applications
JIS G4304 SUS630
Hot-rolled stainless steel plates and strips
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can JIS G4304 SUS630 Be Substituted With GB/T 3280 06Cr19Ni10?
JIS G4304 SUS630 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4304 SUS630
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
JIS G4304 SUS630
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS630 and GB/T 3280 06Cr19Ni10?
JIS G4304 SUS630 specifies Cu, Nb which are not specified for GB/T 3280 06Cr19Ni10.
Can JIS G4304 SUS630 be substituted with GB/T 3280 06Cr19Ni10?
JIS G4304 SUS630 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.