JIS G4304 SUS821L1 vs ASTM A959 S32001

Close Alternative — 77.1% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS821L1 (JIS G4304:2021) and ASTM A959 S32001 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS821L1 is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 S32001 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS821L1 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 S32001 is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS821L1 vs ASTM A959 S32001 is a 77.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.1%.

Frequently Compared With JIS G4304 SUS821L1:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
77.1%
MECHANICAL MATCH
No shared data
OVERALL
77.1%
Specifications
Property JIS G4304 SUS821L1 ASTM A959 S32001
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.75 <=1.00
Mn (%) 2.00-4.00 4.0-6.0
P (%) <=0.040 <=0.040
S (%) <=0.020 <=0.030
Ni (%) 1.50-2.50 1.00-3.00
Cr (%) 20.50-21.50 19.5-21.5
Mo (%) <=0.60 <=0.60
Cu (%) 0.50-1.50 <=1.00
N (%) 0.15-0.20 0.05-0.17
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS821L1 ASTM A959 S32001
Tensile Strength >=600 MPa Not specified
Yield Strength >=400 MPa Not specified
Elongation >=20% Not specified
Hardness <=290 HB Not specified
Condition Solution heat treated plate and strip, thickness up to 2.0 mm for elongation; proof strength applies only when specified Not specified
Typical Applications
JIS G4304 SUS821L1
Hot-rolled stainless steel plates and strips
ASTM A959 S32001
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can JIS G4304 SUS821L1 Be Substituted With ASTM A959 S32001?
JIS G4304 SUS821L1 and ASTM A959 S32001 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4304 SUS821L1
0 active listings and RFQs →
ASTM A959 S32001
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS821L1 and ASTM A959 S32001?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4304 SUS821L1 be substituted with ASTM A959 S32001?
JIS G4304 SUS821L1 and ASTM A959 S32001 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.