Minimal Match — 45.1% match
based on chemical composition and mechanical property overlap.
JIS G4304 SUS836L (JIS G4304:2021) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4304 SUS836L is typically used for hot-rolled stainless steel plates and strips, while EN 10088-1 1.4401 is commonly used for marine, chemical processing, pharmaceutical equipment.
JIS G4304 SUS836L is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.
As per chemical composition, JIS G4304 SUS836L vs EN 10088-1 1.4401 is a 55.1% match.
As per mechanical properties, the match is 25%.
Combined, this makes them a minimal match overall at 45.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4304 SUS836L
EN 10088-1 1.4401
Tensile Strength
>=640 MPa
≥520 MPa
Yield Strength
>=275 MPa
≥210 MPa
Elongation
>=40%
≥40%
Hardness
<=217 HB
≤215 HB
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Not specified
Typical Applications
JIS G4304 SUS836L
Hot-rolled stainless steel plates and strips
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
JIS G4304 SUS836L specifies P, S, N which are not specified for EN 10088-1 1.4401.
Can JIS G4304 SUS836L Be Substituted With EN 10088-1 1.4401?
JIS G4304 SUS836L and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between JIS G4304 SUS836L and EN 10088-1 1.4401?
JIS G4304 SUS836L specifies P, S, N which are not specified for EN 10088-1 1.4401.
Can JIS G4304 SUS836L be substituted with EN 10088-1 1.4401?
JIS G4304 SUS836L and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.