JIS G4305 SUS301L vs EN 10088-1 X4CrNiCu18-7

Close Alternative — 84.2% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS301L (JIS G4305:2012) and EN 10088-1 X4CrNiCu18-7 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS301L is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X4CrNiCu18-7 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4305 SUS301L vs EN 10088-1 X4CrNiCu18-7 is a 84.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.2%.

Frequently Compared With JIS G4305 SUS301L:
IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
84.2%
MECHANICAL MATCH
No shared data
OVERALL
84.2%
Specifications
Property JIS G4305 SUS301L EN 10088-1 X4CrNiCu18-7
Standard JIS G4305:2012 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.05
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Ni (%) 6.00-8.00 6.0-8.0
Cr (%) 16.00-18.00 17.0-19.0
N (%) <=0.20 0.05-0.15
Cu (%) Not specified 0.50-2.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS301L EN 10088-1 X4CrNiCu18-7
Tensile Strength >=550 MPa Not specified
Yield Strength >=215 MPa Not specified
Elongation >=45% Not specified
Hardness <=207 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUS301L
Cold-rolled stainless steel plates, sheet and strip
EN 10088-1 X4CrNiCu18-7
Not documented
Key Differences
Can JIS G4305 SUS301L Be Substituted With EN 10088-1 X4CrNiCu18-7?
JIS G4305 SUS301L and EN 10088-1 X4CrNiCu18-7 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4305 SUS301L
0 active listings and RFQs →
EN 10088-1 X4CrNiCu18-7
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS301L and EN 10088-1 X4CrNiCu18-7?
EN 10088-1 X4CrNiCu18-7 specifies Cu which is not specified for JIS G4305 SUS301L.
Can JIS G4305 SUS301L be substituted with EN 10088-1 X4CrNiCu18-7?
JIS G4305 SUS301L and EN 10088-1 X4CrNiCu18-7 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.