JIS G4305 SUS316LN vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS316LN (JIS G4305:2012) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS316LN is typically used for cold-rolled stainless steel plates, sheet and strip, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. JIS G4305 SUS316LN is defined under Japanese Industrial Standards (JIS), originating from Japan, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, JIS G4305 SUS316LN vs GB/T 3280 06Cr19Ni10 is a 66.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With JIS G4305 SUS316LN:
GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
66.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property JIS G4305 SUS316LN GB/T 3280 06Cr19Ni10
Standard JIS G4305:2012 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08 max
Si (%) <=1.00 1.00 max
Mn (%) <=2.00 2.00 max
P (%) <=0.045 0.045 max
S (%) <=0.030 0.030 max
Ni (%) 10.50-14.50 8.00-11.00
Cr (%) 16.50-18.50 18.00-20.00
Mo (%) 2.00-3.00 Not specified
N (%) 0.12-0.22 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS316LN GB/T 3280 06Cr19Ni10
Tensile Strength >=550 MPa 520-720 MPa
Yield Strength >=245 MPa 205-310 MPa
Elongation >=40% 40-60%
Hardness <=217 HB 187 HB max
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUS316LN
Cold-rolled stainless steel plates, sheet and strip
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can JIS G4305 SUS316LN Be Substituted With GB/T 3280 06Cr19Ni10?
JIS G4305 SUS316LN and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4305 SUS316LN
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
JIS G4305 SUS316LN
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS316LN and GB/T 3280 06Cr19Ni10?
JIS G4305 SUS316LN specifies Mo, N which are not specified for GB/T 3280 06Cr19Ni10.
Can JIS G4305 SUS316LN be substituted with GB/T 3280 06Cr19Ni10?
JIS G4305 SUS316LN and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.