JIS G4305 SUS316N vs EN 10088-1 1.4006

Minimal Match — 32.7% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS316N (JIS G4305:2012) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS316N is typically used for cold-rolled stainless steel plates, sheet and strip, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. JIS G4305 SUS316N is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4305 SUS316N vs EN 10088-1 1.4006 is a 49% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.7%.

Frequently Compared With JIS G4305 SUS316N:
IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
49%
MECHANICAL MATCH
0%
OVERALL
32.7%
Specifications
Property JIS G4305 SUS316N EN 10088-1 1.4006
Standard JIS G4305:2012 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.08–0.15
Si (%) <=1.00 ≤1.00
Mn (%) <=2.00 ≤1.50
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Ni (%) 10.00-14.00 ≤0.75
Cr (%) 16.00-18.00 11.5–13.5
Mo (%) 2.00-3.00 Not specified
N (%) 0.10-0.22 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS316N EN 10088-1 1.4006
Tensile Strength >=550 MPa ≥540 MPa (annealed)
Yield Strength >=275 MPa Not specified
Elongation >=35% ≥18%
Hardness <=217 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
JIS G4305 SUS316N
Cold-rolled stainless steel plates, sheet and strip
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can JIS G4305 SUS316N Be Substituted With EN 10088-1 1.4006?
JIS G4305 SUS316N and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4305 SUS316N
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
JIS G4305 SUS316N
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS316N and EN 10088-1 1.4006?
JIS G4305 SUS316N specifies P, S, Mo, N which are not specified for EN 10088-1 1.4006.
Can JIS G4305 SUS316N be substituted with EN 10088-1 1.4006?
JIS G4305 SUS316N and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.