Strong Match — 87% match
based on chemical composition and mechanical property overlap.
JIS G4305 SUS317 (JIS G4305:2012) and ASTM A276/A276M S31700 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4305 SUS317 is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A276/A276M S31700 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
JIS G4305 SUS317 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A276/A276M S31700 is defined under ASTM International, originating from United States.
As per chemical composition, JIS G4305 SUS317 vs ASTM A276/A276M S31700 is a 97.2% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a strong match overall at 87%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4305 SUS317
ASTM A276/A276M S31700
Tensile Strength
>=520 MPa
>=515 MPa
Yield Strength
>=205 MPa
>=205 MPa
Elongation
>=40%
>=40%
Hardness
<=187 HB
Not specified
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
JIS G4305 SUS317
Cold-rolled stainless steel plates, sheet and strip
ASTM A276/A276M S31700
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
ASTM A276/A276M S31700 specifies N which is not specified for JIS G4305 SUS317.
Can JIS G4305 SUS317 Be Substituted With ASTM A276/A276M S31700?
JIS G4305 SUS317 and ASTM A276/A276M S31700 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S31700 is often considered as a substitute for JIS G4305 SUS317 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G4305 SUS317 and ASTM A276/A276M S31700?
ASTM A276/A276M S31700 specifies N which is not specified for JIS G4305 SUS317.
Can JIS G4305 SUS317 be substituted with ASTM A276/A276M S31700?
JIS G4305 SUS317 and ASTM A276/A276M S31700 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S31700 is often considered as a substitute for JIS G4305 SUS317 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.