JIS G4305 SUS317J2 vs BS 970 (Part 1) 316S33

Related Material — 69.7% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS317J2 (JIS G4305:2012) and BS 970 (Part 1) 316S33 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS317J2 is typically used for cold-rolled stainless steel plates, sheet and strip, while BS 970 (Part 1) 316S33 is commonly used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition).. JIS G4305 SUS317J2 is defined under Japanese Industrial Standards (JIS), originating from Japan, while BS 970 (Part 1) 316S33 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, JIS G4305 SUS317J2 vs BS 970 (Part 1) 316S33 is a 69.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.7%.

Frequently Compared With JIS G4305 SUS317J2:
ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845
Other Stainless Steel Grades to Compare With JIS G4305 SUS317J2:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
69.7%
MECHANICAL MATCH
No shared data
OVERALL
69.7%
Specifications
Property JIS G4305 SUS317J2 BS 970 (Part 1) 316S33
Standard JIS G4305:2012 BS 970 (Part 1):1983
Category Stainless Steel Stainless Steel
C (%) <=0.06 <=0.07
Si (%) <=1.50 <=1.0
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Ni (%) 12.00-16.00 11.0-14.0
Cr (%) 23.00-26.00 16.5-18.5
Mo (%) 0.50-1.20 2.50-3.00
N (%) 0.25-0.40 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS317J2 BS 970 (Part 1) 316S33
Tensile Strength >=690 MPa Not specified
Yield Strength >=345 MPa Not specified
Elongation >=40% Not specified
Hardness <=250 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUS317J2
Cold-rolled stainless steel plates, sheet and strip
BS 970 (Part 1) 316S33
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
Key Differences
Can JIS G4305 SUS317J2 Be Substituted With BS 970 (Part 1) 316S33?
JIS G4305 SUS317J2 and BS 970 (Part 1) 316S33 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4305 SUS317J2
0 active listings and RFQs →
BS 970 (Part 1) 316S33
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS317J2 and BS 970 (Part 1) 316S33?
JIS G4305 SUS317J2 specifies N which is not specified for BS 970 (Part 1) 316S33.
Can JIS G4305 SUS317J2 be substituted with BS 970 (Part 1) 316S33?
JIS G4305 SUS317J2 and BS 970 (Part 1) 316S33 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.