JIS G4305 SUS317LN vs ASTM A959 317L

Strong Match — 94.4% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS317LN (JIS G4305:2012) and ASTM A959 317L (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS317LN is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A959 317L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4305 SUS317LN is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 317L is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4305 SUS317LN vs ASTM A959 317L is a 94.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.4%.

Frequently Compared With JIS G4305 SUS317LN:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
94.4%
MECHANICAL MATCH
No shared data
OVERALL
94.4%
Specifications
Property JIS G4305 SUS317LN ASTM A959 317L
Standard JIS G4305:2012 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Ni (%) 11.00-15.00 11.0-15.0
Cr (%) 18.00-20.00 18.0-20.0
Mo (%) 3.00-4.00 3.0-4.0
N (%) 0.10-0.22 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS317LN ASTM A959 317L
Tensile Strength >=550 MPa Not specified
Yield Strength >=245 MPa Not specified
Elongation >=40% Not specified
Hardness <=217 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUS317LN
Cold-rolled stainless steel plates, sheet and strip
ASTM A959 317L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4305 SUS317LN Be Substituted With ASTM A959 317L?
JIS G4305 SUS317LN and ASTM A959 317L overlap closely enough on chemistry and mechanical properties that ASTM A959 317L is often considered as a substitute for JIS G4305 SUS317LN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
JIS G4305 SUS317LN
0 active listings and RFQs →
ASTM A959 317L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS317LN and ASTM A959 317L?
JIS G4305 SUS317LN specifies N which is not specified for ASTM A959 317L.
Can JIS G4305 SUS317LN be substituted with ASTM A959 317L?
JIS G4305 SUS317LN and ASTM A959 317L overlap closely enough on chemistry and mechanical properties that ASTM A959 317L is often considered as a substitute for JIS G4305 SUS317LN in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.