Strong Match — 100% match
based on chemical composition and mechanical property overlap.
JIS G4305 SUS410S (JIS G4305:2012) and JIS G4304 SUS410S (JIS G4304:2021) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4305 SUS410S is typically used for cold-rolled stainless steel plates, sheet and strip, while JIS G4304 SUS410S is commonly used for hot-rolled stainless steel plates and strips.
JIS G4305 SUS410S is defined under Japanese Industrial Standards (JIS), originating from Japan, while JIS G4304 SUS410S is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, JIS G4305 SUS410S vs JIS G4304 SUS410S is a 100% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 100%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4305 SUS410S
JIS G4304 SUS410S
Tensile Strength
>=410 MPa
>=410 MPa
Yield Strength
>=205 MPa
>=205 MPa
Elongation
>=20%
>=20%
Hardness
<=183 HB
<=183 HB
Condition
Annealed plate and strip; proof strength applies only when specified by the purchaser
Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
JIS G4305 SUS410S
Cold-rolled stainless steel plates, sheet and strip
JIS G4304 SUS410S
Hot-rolled stainless steel plates and strips
Can JIS G4305 SUS410S Be Substituted With JIS G4304 SUS410S?
JIS G4305 SUS410S and JIS G4304 SUS410S overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS410S is often considered as a substitute for JIS G4305 SUS410S in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G4305 SUS410S and JIS G4304 SUS410S?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4305 SUS410S be substituted with JIS G4304 SUS410S?
JIS G4305 SUS410S and JIS G4304 SUS410S overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS410S is often considered as a substitute for JIS G4305 SUS410S in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.