Minimal Match — 33.8% match
based on chemical composition and mechanical property overlap.
JIS G4305 SUS444 (JIS G4305:2012) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4305 SUS444 is typically used for cold-rolled stainless steel plates, sheet and strip, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications.
JIS G4305 SUS444 is defined under Japanese Industrial Standards (JIS) (Japan).
As per chemical composition, JIS G4305 SUS444 vs GOST 5632 06Kh23N28 is a 50.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 33.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4305 SUS444
GOST 5632 06Kh23N28
Tensile Strength
>=410 MPa
≥510 MPa
Yield Strength
>=245 MPa
≥196 MPa
Elongation
>=20%
≥35%
Hardness
<=217 HB
Not specified
Condition
Annealed plate and strip; proof strength applies only when specified by the purchaser
Not specified
Max Service Temp
Not specified
1050°C
Typical Applications
JIS G4305 SUS444
Cold-rolled stainless steel plates, sheet and strip
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
JIS G4305 SUS444 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can JIS G4305 SUS444 Be Substituted With GOST 5632 06Kh23N28?
JIS G4305 SUS444 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between JIS G4305 SUS444 and GOST 5632 06Kh23N28?
JIS G4305 SUS444 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can JIS G4305 SUS444 be substituted with GOST 5632 06Kh23N28?
JIS G4305 SUS444 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.