JIS G4305 SUS630 vs GOST 5632 06Kh23N28

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS630 (JIS G4305:2012) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS630 is typically used for cold-rolled stainless steel plates, sheet and strip, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. JIS G4305 SUS630 is defined under Japanese Industrial Standards (JIS) (Japan).

As per chemical composition, JIS G4305 SUS630 vs GOST 5632 06Kh23N28 is a 60.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With JIS G4305 SUS630:
EN 10088-1 1.4401 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H
Other Stainless Steel Grades to Compare With JIS G4305 SUS630:
EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
60.4%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property JIS G4305 SUS630 GOST 5632 06Kh23N28
Standard JIS G4305:2012 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.07 ≤0.06
Si (%) <=1.00 ≤0.80
Mn (%) <=1.00 ≤2.00
P (%) <=0.040 Not specified
S (%) <=0.030 Not specified
Ni (%) 3.00-5.00 26.0–29.0
Cr (%) 15.00-17.50 22.0–25.0
Cu (%) 3.00-5.00 Not specified
Nb (%) 0.15-0.45 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS630 GOST 5632 06Kh23N28
Hardness <=363 HB Not specified
Condition Solution heat treated plate and strip (no strength values specified; aged conditions are in the blocks) Not specified
Tensile Strength Not specified ≥510 MPa
Yield Strength Not specified ≥196 MPa
Elongation Not specified ≥35%
Max Service Temp Not specified 1050°C
Typical Applications
JIS G4305 SUS630
Cold-rolled stainless steel plates, sheet and strip
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can JIS G4305 SUS630 Be Substituted With GOST 5632 06Kh23N28?
JIS G4305 SUS630 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4305 SUS630
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
JIS G4305 SUS630
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS630 and GOST 5632 06Kh23N28?
JIS G4305 SUS630 specifies P, S, Cu, Nb which are not specified for GOST 5632 06Kh23N28.
Can JIS G4305 SUS630 be substituted with GOST 5632 06Kh23N28?
JIS G4305 SUS630 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.