Close Alternative — 78.9% match
based on chemical composition and mechanical property overlap.
JIS G4305 SUS836L (JIS G4305:2012) and ASTM A276/A276M S32053 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4305 SUS836L is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A276/A276M S32053 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
JIS G4305 SUS836L is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A276/A276M S32053 is defined under ASTM International, originating from United States.
As per chemical composition, JIS G4305 SUS836L vs ASTM A276/A276M S32053 is a 80.8% match.
As per mechanical properties, the match is 75%.
Combined, this makes them a close alternative overall at 78.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4305 SUS836L
ASTM A276/A276M S32053
Tensile Strength
>=640 MPa
>=640 MPa
Yield Strength
>=275 MPa
>=295 MPa
Elongation
>=40%
>=40%
Hardness
<=217 HB
<=217 HB
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
JIS G4305 SUS836L
Cold-rolled stainless steel plates, sheet and strip
ASTM A276/A276M S32053
Stainless steel bars and shapes (hot-finished or cold-finished)
Can JIS G4305 SUS836L Be Substituted With ASTM A276/A276M S32053?
JIS G4305 SUS836L and ASTM A276/A276M S32053 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between JIS G4305 SUS836L and ASTM A276/A276M S32053?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4305 SUS836L be substituted with ASTM A276/A276M S32053?
JIS G4305 SUS836L and ASTM A276/A276M S32053 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.