JIS G4305 SUS836L vs ASTM A959 N08367

Close Alternative — 80.6% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS836L (JIS G4305:2012) and ASTM A959 N08367 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS836L is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A959 N08367 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4305 SUS836L is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 N08367 is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4305 SUS836L vs ASTM A959 N08367 is a 80.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 80.6%.

Frequently Compared With JIS G4305 SUS836L:
ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H
Other Stainless Steel Grades to Compare With JIS G4305 SUS836L:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
80.6%
MECHANICAL MATCH
No shared data
OVERALL
80.6%
Specifications
Property JIS G4305 SUS836L ASTM A959 N08367
Standard JIS G4305:2012 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Ni (%) 24.00-26.00 23.5-25.5
Cr (%) 19.00-24.00 20.0-22.0
Mo (%) 5.00-7.00 6.0-7.0
N (%) <=0.25 0.18-0.25
Cu (%) Not specified <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS836L ASTM A959 N08367
Tensile Strength >=640 MPa Not specified
Yield Strength >=275 MPa Not specified
Elongation >=40% Not specified
Hardness <=217 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUS836L
Cold-rolled stainless steel plates, sheet and strip
ASTM A959 N08367
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4305 SUS836L Be Substituted With ASTM A959 N08367?
JIS G4305 SUS836L and ASTM A959 N08367 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4305 SUS836L
0 active listings and RFQs →
ASTM A959 N08367
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS836L and ASTM A959 N08367?
ASTM A959 N08367 specifies Cu which is not specified for JIS G4305 SUS836L.
Can JIS G4305 SUS836L be substituted with ASTM A959 N08367?
JIS G4305 SUS836L and ASTM A959 N08367 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.