JIS G4305 SUS836L vs EN 10088-1 X1NiCrMoCuN25-20-7

Close Alternative — 77.8% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS836L (JIS G4305:2012) and EN 10088-1 X1NiCrMoCuN25-20-7 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS836L is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X1NiCrMoCuN25-20-7 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4305 SUS836L vs EN 10088-1 X1NiCrMoCuN25-20-7 is a 77.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.8%.

Frequently Compared With JIS G4305 SUS836L:
ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H
Other Stainless Steel Grades to Compare With JIS G4305 SUS836L:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
77.8%
MECHANICAL MATCH
No shared data
OVERALL
77.8%
Specifications
Property JIS G4305 SUS836L EN 10088-1 X1NiCrMoCuN25-20-7
Standard JIS G4305:2012 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.020
Si (%) <=1.00 <=0.75
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.030
S (%) <=0.030 <=0.010
Ni (%) 24.00-26.00 24.0-26.0
Cr (%) 19.00-24.00 19.0-21.0
Mo (%) 5.00-7.00 6.0-7.0
N (%) <=0.25 0.15-0.25
Cu (%) Not specified 0.50-1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS836L EN 10088-1 X1NiCrMoCuN25-20-7
Tensile Strength >=640 MPa Not specified
Yield Strength >=275 MPa Not specified
Elongation >=40% Not specified
Hardness <=217 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUS836L
Cold-rolled stainless steel plates, sheet and strip
EN 10088-1 X1NiCrMoCuN25-20-7
Not documented
Key Differences
Can JIS G4305 SUS836L Be Substituted With EN 10088-1 X1NiCrMoCuN25-20-7?
JIS G4305 SUS836L and EN 10088-1 X1NiCrMoCuN25-20-7 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
JIS G4305 SUS836L
0 active listings and RFQs →
EN 10088-1 X1NiCrMoCuN25-20-7
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS836L and EN 10088-1 X1NiCrMoCuN25-20-7?
EN 10088-1 X1NiCrMoCuN25-20-7 specifies Cu which is not specified for JIS G4305 SUS836L.
Can JIS G4305 SUS836L be substituted with EN 10088-1 X1NiCrMoCuN25-20-7?
JIS G4305 SUS836L and EN 10088-1 X1NiCrMoCuN25-20-7 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.