Strong Match — 100% match
based on chemical composition and mechanical property overlap.
JIS G4305 SUS836L (JIS G4305:2012) and JIS G4304 SUS836L (JIS G4304:2021) are both steel grades.
Both fall under the Stainless Steel category.
JIS G4305 SUS836L is typically used for cold-rolled stainless steel plates, sheet and strip, while JIS G4304 SUS836L is commonly used for hot-rolled stainless steel plates and strips.
JIS G4305 SUS836L is defined under Japanese Industrial Standards (JIS), originating from Japan, while JIS G4304 SUS836L is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, JIS G4305 SUS836L vs JIS G4304 SUS836L is a 100% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 100%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
JIS G4305 SUS836L
JIS G4304 SUS836L
Tensile Strength
>=640 MPa
>=640 MPa
Yield Strength
>=275 MPa
>=275 MPa
Elongation
>=40%
>=40%
Hardness
<=217 HB
<=217 HB
Condition
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
JIS G4305 SUS836L
Cold-rolled stainless steel plates, sheet and strip
JIS G4304 SUS836L
Hot-rolled stainless steel plates and strips
Can JIS G4305 SUS836L Be Substituted With JIS G4304 SUS836L?
JIS G4305 SUS836L and JIS G4304 SUS836L overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS836L is often considered as a substitute for JIS G4305 SUS836L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between JIS G4305 SUS836L and JIS G4304 SUS836L?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can JIS G4305 SUS836L be substituted with JIS G4304 SUS836L?
JIS G4305 SUS836L and JIS G4304 SUS836L overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS836L is often considered as a substitute for JIS G4305 SUS836L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.