JIS G4305 SUS890L vs ASTM A959 904L

Strong Match — 96.9% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS890L (JIS G4305:2012) and ASTM A959 904L (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS890L is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A959 904L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4305 SUS890L is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 904L is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4305 SUS890L vs ASTM A959 904L is a 96.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 96.9%.

Frequently Compared With JIS G4305 SUS890L:
GOST 5632 08X18H10 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
96.9%
MECHANICAL MATCH
No shared data
OVERALL
96.9%
Specifications
Property JIS G4305 SUS890L ASTM A959 904L
Standard JIS G4305:2012 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Ni (%) 23.00-28.00 23.0-28.0
Cr (%) 19.00-23.00 19.0-23.0
Mo (%) 4.00-5.00 4.0-5.0
Cu (%) 1.00-2.00 1.00-2.00
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS890L ASTM A959 904L
Tensile Strength >=490 MPa Not specified
Yield Strength >=215 MPa Not specified
Elongation >=35% Not specified
Hardness <=187 HB Not specified
Condition Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUS890L
Cold-rolled stainless steel plates, sheet and strip
ASTM A959 904L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4305 SUS890L Be Substituted With ASTM A959 904L?
JIS G4305 SUS890L and ASTM A959 904L overlap closely enough on chemistry and mechanical properties that ASTM A959 904L is often considered as a substitute for JIS G4305 SUS890L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
JIS G4305 SUS890L
0 active listings and RFQs →
ASTM A959 904L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS890L and ASTM A959 904L?
ASTM A959 904L specifies N which is not specified for JIS G4305 SUS890L.
Can JIS G4305 SUS890L be substituted with ASTM A959 904L?
JIS G4305 SUS890L and ASTM A959 904L overlap closely enough on chemistry and mechanical properties that ASTM A959 904L is often considered as a substitute for JIS G4305 SUS890L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.