JIS G4305 SUSXM27 (JIS G4305:2012) and ASTM A959 XM-27 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUSXM27 is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A959 XM-27 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4305 SUSXM27 is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 XM-27 is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4305 SUSXM27 vs ASTM A959 XM-27 is a 99.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 99.1%.

Frequently Compared With JIS G4305 SUSXM27:
ASTM A959 29-4 ASTM A959 29-4-2 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
99.1%
MECHANICAL MATCH
No shared data
OVERALL
99.1%
Specifications
Property JIS G4305 SUSXM27 ASTM A959 XM-27
Standard JIS G4305:2012 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.010 <=0.010
Si (%) <=0.40 <=0.40
Mn (%) <=0.40 <=0.40
P (%) <=0.030 <=0.020
S (%) <=0.020 <=0.020
Cr (%) 25.00-27.50 25.0-27.5
Mo (%) 0.75-1.50 0.75-1.50
N (%) <=0.015 <=0.015
Ni (%) <=0.50 <=0.50
Cu (%) <=0.20 <=0.20
Cb (%) Not specified 0.05-0.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUSXM27 ASTM A959 XM-27
Tensile Strength >=410 MPa Not specified
Yield Strength >=245 MPa Not specified
Elongation >=22% Not specified
Hardness <=192 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUSXM27
Cold-rolled stainless steel plates, sheet and strip
ASTM A959 XM-27
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4305 SUSXM27 Be Substituted With ASTM A959 XM-27?
JIS G4305 SUSXM27 and ASTM A959 XM-27 overlap closely enough on chemistry and mechanical properties that ASTM A959 XM-27 is often considered as a substitute for JIS G4305 SUSXM27 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
JIS G4305 SUSXM27
0 active listings and RFQs →
ASTM A959 XM-27
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUSXM27 and ASTM A959 XM-27?
ASTM A959 XM-27 specifies Cb which is not specified for JIS G4305 SUSXM27.
Can JIS G4305 SUSXM27 be substituted with ASTM A959 XM-27?
JIS G4305 SUSXM27 and ASTM A959 XM-27 overlap closely enough on chemistry and mechanical properties that ASTM A959 XM-27 is often considered as a substitute for JIS G4305 SUSXM27 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.