JIS G4305 SUSXM27 vs JIS G4304 SUS436J1L

Related Material — 64.7% match based on chemical composition and mechanical property overlap.

JIS G4305 SUSXM27 (JIS G4305:2012) and JIS G4304 SUS436J1L (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUSXM27 is typically used for cold-rolled stainless steel plates, sheet and strip, while JIS G4304 SUS436J1L is commonly used for hot-rolled stainless steel plates and strips. JIS G4305 SUSXM27 is defined under Japanese Industrial Standards (JIS), originating from Japan, while JIS G4304 SUS436J1L is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, JIS G4305 SUSXM27 vs JIS G4304 SUS436J1L is a 59.5% match. As per mechanical properties, the match is 75%. Combined, this makes them a related material overall at 64.7%.

Frequently Compared With JIS G4305 SUSXM27:
ASTM A959 29-4 ASTM A959 29-4-2 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
59.5%
MECHANICAL MATCH
75%
OVERALL
64.7%
Specifications
Property JIS G4305 SUSXM27 JIS G4304 SUS436J1L
Standard JIS G4305:2012 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.010 <=0.025
Si (%) <=0.40 <=1.00
Mn (%) <=0.40 <=1.00
P (%) <=0.030 <=0.040
S (%) <=0.020 <=0.030
Cr (%) 25.00-27.50 17.00-20.00
Mo (%) 0.75-1.50 0.40-0.80
N (%) <=0.015 <=0.025
Ni (%) <=0.50 <=0.60
Cu (%) <=0.20 Not specified
Ti (%) Not specified <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUSXM27 JIS G4304 SUS436J1L
Tensile Strength >=410 MPa >=410 MPa
Yield Strength >=245 MPa >=245 MPa
Elongation >=22% >=20%
Hardness <=192 HB <=192 HB
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
JIS G4305 SUSXM27
Cold-rolled stainless steel plates, sheet and strip
JIS G4304 SUS436J1L
Hot-rolled stainless steel plates and strips
Key Differences
Can JIS G4305 SUSXM27 Be Substituted With JIS G4304 SUS436J1L?
JIS G4305 SUSXM27 and JIS G4304 SUS436J1L share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4305 SUSXM27
0 active listings and RFQs →
JIS G4304 SUS436J1L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUSXM27 and JIS G4304 SUS436J1L?
JIS G4305 SUSXM27 specifies Cu which is not specified for JIS G4304 SUS436J1L. JIS G4304 SUS436J1L specifies Ti which is not specified for JIS G4305 SUSXM27.
Can JIS G4305 SUSXM27 be substituted with JIS G4304 SUS436J1L?
JIS G4305 SUSXM27 and JIS G4304 SUS436J1L share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.