NF A35-552 XC60 vs BS 970 (Part 3) 070M55

Strong Match — 90.2% match based on chemical composition and mechanical property overlap.

NF A35-552 XC60 (NF A35-552:1986) and BS 970 (Part 3) 070M55 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. NF A35-552 XC60 is typically used for used for springs, knives, wear parts, punches, blades, and high-strength tools., while BS 970 (Part 3) 070M55 is commonly used for used for springs, blades, wear plates, hand tools, shafts, and cutting components.. NF A35-552 XC60 is defined under Association Francaise de Normalisation (NF), originating from France, while BS 970 (Part 3) 070M55 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, NF A35-552 XC60 vs BS 970 (Part 3) 070M55 is a 90.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.2%.

Frequently Compared With NF A35-552 XC60:
BS 970 (Part 1) 040A10 BS 970 (Part 1) 080A20 BS 970 (Part 1) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 045A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A62
Match Breakdown
CHEMISTRY MATCH
90.2%
MECHANICAL MATCH
No shared data
OVERALL
90.2%
Specifications
Property NF A35-552 XC60 BS 970 (Part 3) 070M55
Standard NF A35-552:1986 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) 0.57-0.65 0.50-0.60
Si (%) 0.10-0.35 0.10-0.40
Mn (%) 0.50-0.80 0.50-0.90
P (%) 0.045 max <=0.05
S (%) 0.045 max <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property NF A35-552 XC60 BS 970 (Part 3) 070M55
Tensile Strength 800-950 MPa Not specified
Yield Strength 500-650 MPa Not specified
Elongation 10-16% Not specified
Hardness 220-285 HB Not specified
Typical Applications
NF A35-552 XC60
Used for springs, knives, wear parts, punches, blades, and high-strength tools.
BS 970 (Part 3) 070M55
Used for springs, blades, wear plates, hand tools, shafts, and cutting components.
Can NF A35-552 XC60 Be Substituted With BS 970 (Part 3) 070M55?
NF A35-552 XC60 and BS 970 (Part 3) 070M55 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 070M55 is often considered as a substitute for NF A35-552 XC60 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
NF A35-552 XC60
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5500–5800 mm (216.54–228.35 in)
BS 970 (Part 3) 070M55
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–5800 mm (188.98–228.35 in)
On M-EX Right Now
NF A35-552 XC60
2 active listings and RFQs →
BS 970 (Part 3) 070M55
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between NF A35-552 XC60 and BS 970 (Part 3) 070M55?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can NF A35-552 XC60 be substituted with BS 970 (Part 3) 070M55?
NF A35-552 XC60 and BS 970 (Part 3) 070M55 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 070M55 is often considered as a substitute for NF A35-552 XC60 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.