SAE J404 8620 vs IS 11169 (Part 1) 21Ni2Cr2Mo2

Strong Match — 97.6% match based on chemical composition and mechanical property overlap.

SAE J404 8620 (SAE J404:2009) and IS 11169 (Part 1) 21Ni2Cr2Mo2 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. SAE J404 8620 is typically used for case hardened gears, cams, pins, shafts, while IS 11169 (Part 1) 21Ni2Cr2Mo2 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b). SAE J404 8620 is defined under SAE International, originating from United States, while IS 11169 (Part 1) 21Ni2Cr2Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, SAE J404 8620 vs IS 11169 (Part 1) 21Ni2Cr2Mo2 is a 97.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 97.6%.

Frequently Compared With SAE J404 8620:
GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A NF A35-565 100C6 UNI 11234 100Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
97.6%
MECHANICAL MATCH
No shared data
OVERALL
97.6%
Specifications
Property SAE J404 8620 IS 11169 (Part 1) 21Ni2Cr2Mo2
Standard SAE J404:2009 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.18-0.23 0.18-0.23
Cr (%) 0.40-0.60 0.40-0.60
Mn (%) 0.70-0.90 0.70-0.90
Mo (%) 0.15-0.25 0.15-0.25
Ni (%) 0.40-0.70 0.40-0.70
P (%) <=0.030 <=0.030
S (%) <=0.040 <=0.040
Si (%) 0.15-0.35 0.15-0.35
Cu (%) Not specified <=0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
SAE J404 8620
Case hardened gears, cams, pins, shafts
IS 11169 (Part 1) 21Ni2Cr2Mo2
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can SAE J404 8620 Be Substituted With IS 11169 (Part 1) 21Ni2Cr2Mo2?
SAE J404 8620 and IS 11169 (Part 1) 21Ni2Cr2Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 21Ni2Cr2Mo2 is often considered as a substitute for SAE J404 8620 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
SAE J404 8620
Round Bar → (8 listings)
Diameter: 50–75 mm (1.97–2.95 in)
Length: 5200–7000 mm (204.72–275.59 in)
Flat Bar → (3 listings)
Thickness: 30–30 mm (1.18–1.18 in)
Width: 150–150 mm (5.91–5.91 in)
Length: 3200–3400 mm (125.98–133.86 in)
IS 11169 (Part 1) 21Ni2Cr2Mo2
No active listings currently.
On M-EX Right Now
SAE J404 8620
11 active listings and RFQs →
IS 11169 (Part 1) 21Ni2Cr2Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SAE J404 8620 and IS 11169 (Part 1) 21Ni2Cr2Mo2?
IS 11169 (Part 1) 21Ni2Cr2Mo2 specifies Cu which is not specified for SAE J404 8620.
Can SAE J404 8620 be substituted with IS 11169 (Part 1) 21Ni2Cr2Mo2?
SAE J404 8620 and IS 11169 (Part 1) 21Ni2Cr2Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 21Ni2Cr2Mo2 is often considered as a substitute for SAE J404 8620 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.