SAE J403 1026 vs IS 11169 (Part 1) 25C8

Strong Match — 95.4% match based on chemical composition and mechanical property overlap.

SAE J403 1026 (SAE J403:2009) and IS 11169 (Part 1) 25C8 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Carbon Steel category. SAE J403 1026 is typically used for chemistry-only grade; product scope as listed in the composition notes, while IS 11169 (Part 1) 25C8 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). SAE J403 1026 is defined under SAE International, originating from United States, while IS 11169 (Part 1) 25C8 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, SAE J403 1026 vs IS 11169 (Part 1) 25C8 is a 95.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95.4%.

Frequently Compared With SAE J403 1026:
BS 970 (Part 1) 070M26 BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
95.4%
MECHANICAL MATCH
No shared data
OVERALL
95.4%
Specifications
Property SAE J403 1026 IS 11169 (Part 1) 25C8
Standard SAE J403:2009 IS 11169 (Part 1):1984
Category Carbon Steel Carbon Steel
C (%) 0.22-0.28 0.20-0.30
Mn (%) 0.60-0.90 0.60-0.90
P (%) <=0.030 Not specified
S (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SAE J403 1026 IS 11169 (Part 1) 25C8
Tensile Strength (hardened and tempered) Not specified 580-730 MPa (16 mm) / 540-690 MPa (40 mm)
0.2% Proof Stress Not specified >=390 MPa (16 mm) / >=330 MPa (40 mm)
Elongation Not specified >=18% (16 mm) / >=20% (40 mm)
Hardness, annealed Not specified <=150 HB
Typical Applications
SAE J403 1026
Chemistry-only grade; product scope as listed in the composition notes
IS 11169 (Part 1) 25C8
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can SAE J403 1026 Be Substituted With IS 11169 (Part 1) 25C8?
SAE J403 1026 and IS 11169 (Part 1) 25C8 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 25C8 is often considered as a substitute for SAE J403 1026 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
SAE J403 1026
0 active listings and RFQs →
IS 11169 (Part 1) 25C8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SAE J403 1026 and IS 11169 (Part 1) 25C8?
SAE J403 1026 specifies P, S which are not specified for IS 11169 (Part 1) 25C8.
Can SAE J403 1026 be substituted with IS 11169 (Part 1) 25C8?
SAE J403 1026 and IS 11169 (Part 1) 25C8 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 25C8 is often considered as a substitute for SAE J403 1026 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.