Strong Match — 90.3% match
based on chemical composition and mechanical property overlap.
SAE J403 1002 (SAE J403:2014) and DIN 1654-2 C8C (DIN 1654-2:1989-10) are both steel grades.
Both fall under the Carbon Steel category.
SAE J403 1002 is typically used for chemistry-only grade; product scope as listed in the composition notes, while DIN 1654-2 C8C is commonly used for wire drawing, cold heading, nails.
SAE J403 1002 is defined under SAE International, originating from United States, while DIN 1654-2 C8C is defined under Deutsches Institut fur Normung (DIN), originating from Germany.
As per chemical composition, SAE J403 1002 vs DIN 1654-2 C8C is a 90.3% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 90.3%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
SAE J403 1002
DIN 1654-2 C8C
Tensile Strength
Not specified
300–420 MPa
Elongation
Not specified
≥30%
Typical Applications
SAE J403 1002
Chemistry-only grade; product scope as listed in the composition notes
DIN 1654-2 C8C
Wire drawing, cold heading, nails
Can SAE J403 1002 Be Substituted With DIN 1654-2 C8C?
SAE J403 1002 and DIN 1654-2 C8C overlap closely enough on chemistry and mechanical properties that DIN 1654-2 C8C is often considered as a substitute for SAE J403 1002 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between SAE J403 1002 and DIN 1654-2 C8C?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SAE J403 1002 be substituted with DIN 1654-2 C8C?
SAE J403 1002 and DIN 1654-2 C8C overlap closely enough on chemistry and mechanical properties that DIN 1654-2 C8C is often considered as a substitute for SAE J403 1002 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.