SAE J403 1070 vs AISI 1060

Strong Match — 91.4% match based on chemical composition and mechanical property overlap.

SAE J403 1070 (SAE J403:2014) and AISI 1060 are both steel grades. Both fall under the Carbon Steel category. SAE J403 1070 is typically used for chemistry-only grade; product scope as listed in the composition notes, while AISI 1060 is commonly used for used for springs, blades, hand tools, wear parts, shafts, and cutting tools.. SAE J403 1070 is defined under SAE International, originating from United States, while AISI 1060 is defined under AISI, originating from United States.

As per chemical composition, SAE J403 1070 vs AISI 1060 is a 91.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.4%.

Frequently Compared With SAE J403 1070:
BS 970 (Part 1) 060A67 BS 970 (Part 1) 070A67 BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
91.4%
MECHANICAL MATCH
No shared data
OVERALL
91.4%
Specifications
Property SAE J403 1070 AISI 1060
Standard SAE J403:2014 AISI
Category Carbon Steel Carbon Steel
C (%) 0.65-0.75 0.55-0.65
Mn (%) 0.60-0.90 0.60-0.90
P (%) <=0.030 (flat rolled), <=0.040 (long products) ≤0.030
S (%) <=0.035 (flat rolled), <=0.050 (long products) 0.050 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SAE J403 1070 AISI 1060
Condition Not specified Hot Rolled
Tensile Strength Not specified 700-750 MPa
Yield Strength Not specified 380-420 MPa
Elongation Not specified 11-16%
Hardness Not specified 197-220 HB
Typical Applications
SAE J403 1070
Chemistry-only grade; product scope as listed in the composition notes
AISI 1060
Used for springs, blades, hand tools, wear parts, shafts, and cutting tools.
Can SAE J403 1070 Be Substituted With AISI 1060?
SAE J403 1070 and AISI 1060 overlap closely enough on chemistry and mechanical properties that AISI 1060 is often considered as a substitute for SAE J403 1070 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
SAE J403 1070
No active listings currently.
AISI 1060
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5300–6500 mm (208.66–255.91 in)
On M-EX Right Now
SAE J403 1070
0 active listings and RFQs →
AISI 1060
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between SAE J403 1070 and AISI 1060?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SAE J403 1070 be substituted with AISI 1060?
SAE J403 1070 and AISI 1060 overlap closely enough on chemistry and mechanical properties that AISI 1060 is often considered as a substitute for SAE J403 1070 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.