SAE J404 5140 vs UNI 11234 100Cr6

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

SAE J404 5140 (SAE J404:2000) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. SAE J404 5140 is typically used for chemistry-only alloy steel grade; see the composition notes for product scope, while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. SAE J404 5140 is defined under SAE International, originating from United States, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.

As per chemical composition, SAE J404 5140 vs UNI 11234 100Cr6 is a 75.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With SAE J404 5140:
NF A35-565 100C6 IS 11169 (Part 1) 10Ni5Cr4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 103Cr4
Match Breakdown
CHEMISTRY MATCH
75.6%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property SAE J404 5140 UNI 11234 100Cr6
Standard SAE J404:2000 UNI 11234:2007
Category Alloy Steel Alloy Steel
C (%) 0.38-0.43 0.93-1.05
Cr (%) 0.70-0.90 1.35-1.65
Mn (%) 0.70-0.90 0.25-0.45
P (%) <=0.030 <=0.025
S (%) <=0.040 <=0.025
Si (%) 0.15-0.35 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SAE J404 5140 UNI 11234 100Cr6
Tensile Strength Not specified 750-1000 MPa
Yield Strength Not specified 400-600 MPa
Elongation Not specified 10-14 %
Hardness Not specified 60-64 HRC
Typical Applications
SAE J404 5140
Chemistry-only alloy steel grade; see the composition notes for product scope
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Can SAE J404 5140 Be Substituted With UNI 11234 100Cr6?
SAE J404 5140 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
SAE J404 5140
No active listings currently.
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
SAE J404 5140
0 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between SAE J404 5140 and UNI 11234 100Cr6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SAE J404 5140 be substituted with UNI 11234 100Cr6?
SAE J404 5140 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.