Strong Match — 99.6% match
based on chemical composition and mechanical property overlap.
SAE J404 8617 (SAE J404:2000) and AISI 8617 are both steel grades.
Both fall under the Alloy Steel category.
SAE J404 8617 is typically used for chemistry-only alloy steel grade; see the composition notes for product scope, while AISI 8617 is commonly used for used for gears, camshafts, transmission parts, pinions, bearings, and heavy-duty mechanical components..
SAE J404 8617 is defined under SAE International, originating from United States, while AISI 8617 is defined under AISI, originating from United States.
As per chemical composition, SAE J404 8617 vs AISI 8617 is a 99.6% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 99.6%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
SAE J404 8617
AISI 8617
Tensile Strength
Not specified
720-920 MPa
Yield Strength
Not specified
520-720 MPa
Elongation
Not specified
12-18%
Hardness
Not specified
190-250 HB
Typical Applications
SAE J404 8617
Chemistry-only alloy steel grade; see the composition notes for product scope
AISI 8617
Used for gears, camshafts, transmission parts, pinions, bearings, and heavy-duty mechanical components.
Can SAE J404 8617 Be Substituted With AISI 8617?
SAE J404 8617 and AISI 8617 overlap closely enough on chemistry and mechanical properties that AISI 8617 is often considered as a substitute for SAE J404 8617 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between SAE J404 8617 and AISI 8617?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SAE J404 8617 be substituted with AISI 8617?
SAE J404 8617 and AISI 8617 overlap closely enough on chemistry and mechanical properties that AISI 8617 is often considered as a substitute for SAE J404 8617 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.