SAE J404 8627 vs IS 11169 (Part 1) 10Ni5Cr4

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

SAE J404 8627 (SAE J404:2000) and IS 11169 (Part 1) 10Ni5Cr4 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. SAE J404 8627 is typically used for chemistry-only alloy steel grade; see the composition notes for product scope, while IS 11169 (Part 1) 10Ni5Cr4 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b). SAE J404 8627 is defined under SAE International, originating from United States, while IS 11169 (Part 1) 10Ni5Cr4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, SAE J404 8627 vs IS 11169 (Part 1) 10Ni5Cr4 is a 56.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With SAE J404 8627:
NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 07Cr4Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
56.7%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property SAE J404 8627 IS 11169 (Part 1) 10Ni5Cr4
Standard SAE J404:2000 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.25-0.30 0.07-0.12
Cr (%) 0.40-0.60 0.90-1.20
Mn (%) 0.70-0.90 0.60-0.90
Mo (%) 0.15-0.25 Not specified
Ni (%) 0.40-0.70 1.20-1.50
P (%) <=0.030 <=0.025
S (%) <=0.040 <=0.025
Si (%) 0.15-0.35 <=0.30
Cu (%) Not specified <=0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SAE J404 8627 IS 11169 (Part 1) 10Ni5Cr4
Hardness, ferrite-pearlite (+FP) Not specified 137-187 HB
Tensile Strength, annealed (+AC) Not specified <=520 MPa (over 5 to 40 mm)
Typical Applications
SAE J404 8627
Chemistry-only alloy steel grade; see the composition notes for product scope
IS 11169 (Part 1) 10Ni5Cr4
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can SAE J404 8627 Be Substituted With IS 11169 (Part 1) 10Ni5Cr4?
SAE J404 8627 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
SAE J404 8627
0 active listings and RFQs →
IS 11169 (Part 1) 10Ni5Cr4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SAE J404 8627 and IS 11169 (Part 1) 10Ni5Cr4?
SAE J404 8627 specifies Mo which is not specified for IS 11169 (Part 1) 10Ni5Cr4. IS 11169 (Part 1) 10Ni5Cr4 specifies Cu which is not specified for SAE J404 8627.
Can SAE J404 8627 be substituted with IS 11169 (Part 1) 10Ni5Cr4?
SAE J404 8627 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.