Related Material — 56.1% match based on chemical composition and mechanical property overlap.

SAE J404 8627 (SAE J404:2009) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. SAE J404 8627 is defined under SAE International, originating from United States, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, SAE J404 8627 vs IS 4367 07Cr4Mo6 is a 56.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 56.1%.

Frequently Compared With SAE J404 8627:
IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
56.1%
MECHANICAL MATCH
No shared data
OVERALL
56.1%
Specifications
Property SAE J404 8627 IS 4367 07Cr4Mo6
Standard SAE J404:2009 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.25-0.30 <=0.12
Cr (%) 0.40-0.60 0.70-1.10
Mn (%) 0.70-0.90 0.40-0.70
Mo (%) 0.15-0.25 0.45-0.65
Ni (%) 0.40-0.70 <=0.30
P (%) <=0.030 <=0.035
S (%) <=0.040 <=0.035
Si (%) 0.15-0.35 0.15-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SAE J404 8627 IS 4367 07Cr4Mo6
Tensile Strength Not specified 380-550 MPa
Yield Strength Not specified 225 MPa min
Elongation Not specified >=19%
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Condition Not specified Normalised and tempered, ruling section up to 40 mm
Typical Applications
SAE J404 8627
Chemistry-only alloy steel grade; see the composition notes for product scope
IS 4367 07Cr4Mo6
Not documented
Can SAE J404 8627 Be Substituted With IS 4367 07Cr4Mo6?
SAE J404 8627 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
SAE J404 8627
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SAE J404 8627 and IS 4367 07Cr4Mo6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SAE J404 8627 be substituted with IS 4367 07Cr4Mo6?
SAE J404 8627 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.