SAE J404 9260 vs IS 4367 37Mn5Si5

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

SAE J404 9260 (SAE J404:2009) and IS 4367 37Mn5Si5 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. SAE J404 9260 is defined under SAE International, originating from United States, while IS 4367 37Mn5Si5 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, SAE J404 9260 vs IS 4367 37Mn5Si5 is a 79.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With SAE J404 9260:
IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 07Cr4Mo6
Match Breakdown
CHEMISTRY MATCH
79.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property SAE J404 9260 IS 4367 37Mn5Si5
Standard SAE J404:2009 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.56-0.64 0.33-0.41
Mn (%) 0.75-1.00 1.10-1.40
P (%) <=0.030 <=0.035
S (%) <=0.040 <=0.035
Si (%) 1.80-2.20 1.10-1.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SAE J404 9260 IS 4367 37Mn5Si5
Tensile Strength Not specified 780-930 MPa
Yield Strength Not specified 590 MPa min
Elongation Not specified >=14%
Hardness (soft annealed) Not specified <=217 HB
Condition Not specified Hardened and tempered
Typical Applications
SAE J404 9260
Chemistry-only alloy steel grade; see the composition notes for product scope
IS 4367 37Mn5Si5
Not documented
Can SAE J404 9260 Be Substituted With IS 4367 37Mn5Si5?
SAE J404 9260 and IS 4367 37Mn5Si5 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
SAE J404 9260
0 active listings and RFQs →
IS 4367 37Mn5Si5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SAE J404 9260 and IS 4367 37Mn5Si5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SAE J404 9260 be substituted with IS 4367 37Mn5Si5?
SAE J404 9260 and IS 4367 37Mn5Si5 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.