SS 14 23 12 2312 vs IS 1570 (Part 3) 10C8S10

Related Material — 60.4% match based on chemical composition and mechanical property overlap.

SS 14 23 12 2312 and IS 1570 (Part 3) 10C8S10 (IS 1570 (Part 3):1979) are both steel grades. Both fall under the Free Machining Steel category. SS 14 23 12 2312 is defined under Swedish Standards (SS), originating from Sweden, while IS 1570 (Part 3) 10C8S10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, SS 14 23 12 2312 vs IS 1570 (Part 3) 10C8S10 is a 76.8% match. As per mechanical properties, the match is 27.5%. Combined, this makes them a related material overall at 60.4%.

Frequently Compared With SS 14 23 12 2312:
SAE J403 1141 SAE J403 1144 SAE J403 1117 SAE J403 1117 SAE J403 1118 SAE J403 1126 IS 4432 10C8S10 SAE J403 1117 SAE J403 1118 SAE J403 1118 SAE J403 1126 SAE J403 1126
Match Breakdown
CHEMISTRY MATCH
76.8%
MECHANICAL MATCH
27.5%
OVERALL
60.4%
Specifications
Property SS 14 23 12 2312 IS 1570 (Part 3) 10C8S10
Standard SS 14 23 12 IS 1570 (Part 3):1979
Category Free Machining Steel Free Machining Steel
C (%) 0.08-0.15 <=0.15
Si (%) <=0.05 0.05-0.30
Mn (%) 1.00-1.50 0.60-0.90
P (%) <=0.110 <=0.060
S (%) 0.24-0.35 0.08-0.13
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SS 14 23 12 2312 IS 1570 (Part 3) 10C8S10
Tensile Strength 380-570 MPa 370-490 MPa
Yield Strength 240 MPa min Not specified
Elongation 16-22 % >=24%
Hardness 100-170 HB Not specified
Condition Not specified Hot rolled or normalized bars, billets and forgings (Table 2), ruling sections up to 150 mm
Typical Applications
SS 14 23 12 2312
precision turned parts,bushes,fittings,studs,nuts,automatic lathe components,small machined parts
IS 1570 (Part 3) 10C8S10
Not documented
Can SS 14 23 12 2312 Be Substituted With IS 1570 (Part 3) 10C8S10?
SS 14 23 12 2312 and IS 1570 (Part 3) 10C8S10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
SS 14 23 12 2312
Hex Bar → (2 listings)
Across Flats: 25–25 mm (0.98–0.98 in)
Length: 3100–3700 mm (122.05–145.67 in)
IS 1570 (Part 3) 10C8S10
No active listings currently.
On M-EX Right Now
SS 14 23 12 2312
2 active listings and RFQs →
IS 1570 (Part 3) 10C8S10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between SS 14 23 12 2312 and IS 1570 (Part 3) 10C8S10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SS 14 23 12 2312 be substituted with IS 1570 (Part 3) 10C8S10?
SS 14 23 12 2312 and IS 1570 (Part 3) 10C8S10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.