Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
UNS C26000 and UNS C23000 are both brass grades.
Both fall under the Brass Alloys category.
UNS C26000 is defined under Unified Numbering System (UNS), originating from United States, while UNS C23000 is defined under Unified Numbering System (UNS), originating from United States.
As per chemical composition, UNS C26000 vs UNS C23000 is a 79% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
UNS C26000
UNS C23000
Yield Strength
~170-220 MPa (H02 half-hard)
~70 MPa (O60 annealed)
Tensile Strength
~350-390 MPa (H02 half-hard)
~240 MPa (O60 annealed)
Elongation
~35-55% (H02 half-hard)
~25% (O60 annealed)
Note
Cartridge brass, values for H02 half-hard temper
Red brass, values for O60 soft annealed condition
Can UNS C26000 Be Substituted With UNS C23000?
UNS C26000 and UNS C23000 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between UNS C26000 and UNS C23000?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can UNS C26000 be substituted with UNS C23000?
UNS C26000 and UNS C23000 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.