Minimal Match — 48.1% match
based on chemical composition and mechanical property overlap.
UNS C26000 and UNS C36000 are both brass grades.
Both fall under the Brass Alloys category.
UNS C26000 is defined under Unified Numbering System (UNS), originating from United States, while UNS C36000 is defined under Unified Numbering System (UNS), originating from United States.
As per chemical composition, UNS C26000 vs UNS C36000 is a 65.5% match.
As per mechanical properties, the match is 13.3%.
Combined, this makes them a minimal match overall at 48.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
UNS C26000
UNS C36000
Yield Strength
~170-220 MPa (H02 half-hard)
~250-350 MPa (H02 half-hard)
Tensile Strength
~350-390 MPa (H02 half-hard)
~350-450 MPa (H02 half-hard)
Elongation
~35-55% (H02 half-hard)
~10-25% (H02 half-hard)
Note
Cartridge brass, values for H02 half-hard temper
Free-cutting brass, values for H02 half-hard temper
Can UNS C26000 Be Substituted With UNS C36000?
UNS C26000 and UNS C36000 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between UNS C26000 and UNS C36000?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can UNS C26000 be substituted with UNS C36000?
UNS C26000 and UNS C36000 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.