EN 10083-3 41Cr4 Steel: Supply & Demand
Buyer RFQ demand against seller listing supply for EN 10083-3 41Cr4, broken down by form. Signals are indicative and derived from listings and RFQs.
Last updated: 16 Oct 2026, 7:00 AM
Live Signal: This grade’s supply and demand by form, from listings and RFQs open right now. Use this to act today. For example, “Is there a buyer gap in this grade’s round bar this week?”
| Form |
Supply |
Demand |
Status |
Price Band (Rs./MT) |
| Round Bar |
2 |
0 |
Low Activity |
Insufficient data
|
Disclaimer: All information on this page is indicative only and derived from posted listings and RFQs on M-EX. It does not constitute a market price quote or investment advice. M-EX and GTE make no representations as to accuracy or completeness. Actual activity depends on quantity, quality, payment terms and other commercial factors agreed between buyers and sellers.
EN 10083-3 41Cr4 is an Alloy Steel grade: A chromium alloy steel for quenching and tempering to EN 10083-3:2006 (steel number 1.7035), also used for flame or induction hardening. Supplied as semi-finished products, bars, rod, wide flats, hot rolled strip, sheet and plate, and forgings. Quenched and tempered tensile strength 1000 to 1200 MPa for ruling sections up to 16 mm.
Typical applications: Used in shafts, gears, bolts, axles, and automotive components..
Equivalent / Similar Grades (8)
| Grade |
Standard |
Region |
|
ISO 41Cr4
|
ISO 683-1:1987 |
International |
|
DIN 41Cr4 (1.7035)
|
DIN |
Germany |
|
BS 530M40
|
BS |
UK |
|
NF 42 C 4
|
NF |
France |
|
UNI 41Cr4
|
UNI |
Italy |
|
UNE 42Cr4 (F1202)
|
UNE |
Spain |
|
530M40
|
BS 970 (Part 3) |
UK |
|
530H40
|
BS 970 (Part 1) |
UK |
Chemical Composition (%)
| C |
Cr |
Mn |
P |
S |
Si |
| 0.38-0.45 |
0.90-1.20 |
0.60-0.90 |
<=0.025 |
<=0.035 |
<=0.40 |
Mechanical Properties
| Condition |
Quenched and tempered (+QT), ruling section d <= 16 mm |
| Elongation |
11% min |
| Hardness |
Soft annealed (+A): 241 HBW max |
| Tensile Strength |
1000 to 1200 MPa |
| Yield Strength |
800 MPa min |