AISI 1060 vs BS 970 (Part 3) 045A10

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

AISI 1060 and BS 970 (Part 3) 045A10 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. AISI 1060 is typically used for used for springs, blades, hand tools, wear parts, shafts, and cutting tools., while BS 970 (Part 3) 045A10 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (table 14). AISI 1060 is defined under AISI, originating from United States, while BS 970 (Part 3) 045A10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, AISI 1060 vs BS 970 (Part 3) 045A10 is a 80% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With AISI 1060:
BS 970 (Part 1) 080A20 BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 060A62 BS 970 (Part 1) 060A57 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10
Match Breakdown
CHEMISTRY MATCH
80%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property AISI 1060 BS 970 (Part 3) 045A10
Standard AISI BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) 0.55-0.65 0.08-0.13
Mn (%) 0.60-0.90 0.30-0.60
P (%) ≤0.030 <=0.05
S (%) 0.050 max <=0.05
Si (%) Not specified 0.10-0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AISI 1060 BS 970 (Part 3) 045A10
Condition Hot Rolled Not specified
Tensile Strength 700-750 MPa Not specified
Yield Strength 380-420 MPa Not specified
Elongation 11-16% Not specified
Hardness 197-220 HB Not specified
Typical Applications
AISI 1060
Used for springs, blades, hand tools, wear parts, shafts, and cutting tools.
BS 970 (Part 3) 045A10
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (Table 14)
Key Differences
Can AISI 1060 Be Substituted With BS 970 (Part 3) 045A10?
AISI 1060 and BS 970 (Part 3) 045A10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
AISI 1060
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5300–6500 mm (208.66–255.91 in)
BS 970 (Part 3) 045A10
No active listings currently.
On M-EX Right Now
AISI 1060
2 active listings and RFQs →
BS 970 (Part 3) 045A10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between AISI 1060 and BS 970 (Part 3) 045A10?
BS 970 (Part 3) 045A10 specifies Si which is not specified for AISI 1060.
Can AISI 1060 be substituted with BS 970 (Part 3) 045A10?
AISI 1060 and BS 970 (Part 3) 045A10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.