Post Stock Login Register

AISI 8617 vs NF A35-565 100C6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

AISI 8617 and NF A35-565 100C6 are both steel grades. Both fall under the Alloy Steel category. AISI 8617 is typically used for used for gears, camshafts, transmission parts, pinions, bearings, and heavy-duty mechanical components., while NF A35-565 100C6 is commonly used for ball bearings, roller bearings, bearing races, rollers, precision tools, wear resistant parts. AISI 8617 is defined under AISI, originating from United States, while NF A35-565 100C6 is defined under Association Francaise de Normalisation (NF), originating from France.

As per chemical composition, AISI 8617 vs NF A35-565 100C6 is a 58.3% match. As per mechanical properties, the match is 9.2%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With AISI 8617:
UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
58.3%
MECHANICAL MATCH
9.2%
OVERALL
35%
Specifications
Property AISI 8617 NF A35-565 100C6
Standard AISI NF A35-565
Category Alloy Steel Alloy Steel
C (%) 0.15-0.20 0.95-1.05
Mn (%) 0.70-0.90 0.25-0.45
Si (%) 0.15-0.35 0.15-0.35
Ni (%) 0.40-0.70 Not specified
Cr (%) 0.40-0.60 1.35-1.65
Mo (%) 0.15-0.25 Not specified
P (%) 0.035 max <=0.027
S (%) 0.040 max <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AISI 8617 NF A35-565 100C6
Tensile Strength 720-920 MPa 850-1100 MPa
Yield Strength 520-720 MPa Not specified
Elongation 12-18% Not specified
Hardness 190-250 HB 60-66 HRC
Typical Applications
AISI 8617
Used for gears, camshafts, transmission parts, pinions, bearings, and heavy-duty mechanical components.
NF A35-565 100C6
ball bearings, roller bearings, bearing races, rollers, precision tools, wear resistant parts
Key Differences
Can AISI 8617 Be Substituted With NF A35-565 100C6?
AISI 8617 and NF A35-565 100C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
AISI 8617
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5100–6600 mm (200.79–259.84 in)
NF A35-565 100C6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6700–6700 mm (263.78–263.78 in)
On M-EX Right Now
AISI 8617
2 active listings and RFQs →
NF A35-565 100C6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between AISI 8617 and NF A35-565 100C6?
AISI 8617 specifies Ni, Mo which are not specified for NF A35-565 100C6.
Can AISI 8617 be substituted with NF A35-565 100C6?
AISI 8617 and NF A35-565 100C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.