Post Stock Login Register

AISI D2 KNL vs GOST 5950 3H2W8F

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

AISI D2 KNL (ASTM A681) and GOST 5950 3H2W8F (GOST 5950-2000) are both steel grades. Both fall under the Tool & Die Steels category. AISI D2 KNL is typically used for blanking dies, forming dies, thread rolling dies, punches, shear blades, gauges, broaches, drawing dies, while GOST 5950 3H2W8F is commonly used for used for forging dies, extrusion tools, hot punches, mandrels, and die inserts.. AISI D2 KNL is defined under AISI (United States).

As per chemical composition, AISI D2 KNL vs GOST 5950 3H2W8F is a 56.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With AISI D2 KNL:
DIN EN ISO 4957 1.2379 EN ISO 683-17 100Cr6 GB/T 1299 3Cr2W8V DIN EN ISO 4957 1.2344 EN ISO 4957 1.2316 GB/T 1299 4Cr5MoSiV GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS GOST 5950 4H5MFS1 AISI 52100 IS 1570 (Part 6) 103T3 IS 3748 103T3
Match Breakdown
CHEMISTRY MATCH
56.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property AISI D2 KNL GOST 5950 3H2W8F
Standard ASTM A681 GOST 5950-2000
Category Tool & Die Steels Tool & Die Steels
C (%) 1.40–1.60 0.3-0.4
Mn (%) ≤0.60 Not specified
Si (%) ≤0.40 0.2-0.5
Cr (%) 11.00–13.00 2.2-2.7
Mo (%) 0.70–1.20 Not specified
V (%) ≤1.00 0.3-0.6
S (%) ≤0.030 Not specified
P (%) ≤0.030 Not specified
W (%) Not specified 7.5-9.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AISI D2 KNL GOST 5950 3H2W8F
Hardness (annealed) ≤255 HB Not specified
Hardness (hardened) 58–62 HRC Not specified
Compressive Strength 2600 MPa Not specified
Tensile Strength Not specified 1400-1700 MPa
Yield Strength Not specified 1200 MPa min
Elongation Not specified 8% min
Hardness Not specified 45-50 HRC
Typical Applications
AISI D2 KNL
Blanking dies, forming dies, thread rolling dies, punches, shear blades, gauges, broaches, drawing dies
GOST 5950 3H2W8F
Used for forging dies, extrusion tools, hot punches, mandrels, and die inserts.
Key Differences
Can AISI D2 KNL Be Substituted With GOST 5950 3H2W8F?
AISI D2 KNL and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
AISI D2 KNL
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2500–3600 mm (98.43–141.73 in)
GOST 5950 3H2W8F
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–4300 mm (110.24–169.29 in)
On M-EX Right Now
AISI D2 KNL
2 active listings and RFQs →
GOST 5950 3H2W8F
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between AISI D2 KNL and GOST 5950 3H2W8F?
AISI D2 KNL specifies Mn, Mo, S, P which are not specified for GOST 5950 3H2W8F. GOST 5950 3H2W8F specifies W which is not specified for AISI D2 KNL.
Can AISI D2 KNL be substituted with GOST 5950 3H2W8F?
AISI D2 KNL and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.