ASTM A681 P2 vs GB/T 1299 3Cr2W8V

Minimal Match — 33% match based on chemical composition and mechanical property overlap.

ASTM A681 P2 (ASTM A681:2008) and GB/T 1299 3Cr2W8V (GB/T 1299-2014) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 P2 is typically used for injection mould cavities, die casting dies for zinc, while GB/T 1299 3Cr2W8V is commonly used for used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.. ASTM A681 P2 is defined under ASTM International, originating from United States, while GB/T 1299 3Cr2W8V is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, ASTM A681 P2 vs GB/T 1299 3Cr2W8V is a 49.5% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 33%.

Frequently Compared With ASTM A681 P2:
EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 GOST 5950 3H2W8F EN ISO 683-17 100Cr6 GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS1 DIN EN ISO 4957 1.2344 GB/T 1299 4Cr5MoSiV GOST 5950 4H5MFS AISI 52100 IS 3748 103T3 IS 1570 (Part 6) 103T3
Match Breakdown
CHEMISTRY MATCH
49.5%
MECHANICAL MATCH
0%
OVERALL
33%
Specifications
Property ASTM A681 P2 GB/T 1299 3Cr2W8V
Standard ASTM A681:2008 GB/T 1299-2014
Category Tool & Die Steels Tool & Die Steels
C (%) <=0.10 0.30-0.40
Mn (%) 0.10-0.40 0.20-0.50
P (%) <=0.030 0.030 max
S (%) <=0.030 0.030 max
Si (%) 0.10-0.40 0.20-0.40
Cr (%) 0.75-1.25 2.20-2.70
Mo (%) 0.15-0.40 Not specified
Ni (%) 0.10-0.50 Not specified
W (%) Not specified 7.50-9.00
V (%) Not specified 0.20-0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 P2 GB/T 1299 3Cr2W8V
Hardness <=100 HB 48-54 HRC
Condition Annealed (maximum Brinell hardness) Not specified
Tensile Strength Not specified 1180-1380 MPa
Yield Strength Not specified 980-1180 MPa
Elongation Not specified 10-14%
Typical Applications
ASTM A681 P2
Injection mould cavities, die casting dies for zinc
GB/T 1299 3Cr2W8V
Used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.
Key Differences
Can ASTM A681 P2 Be Substituted With GB/T 1299 3Cr2W8V?
ASTM A681 P2 and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A681 P2
Round Bar → (3 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2700–3900 mm (106.3–153.54 in)
GB/T 1299 3Cr2W8V
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–2900 mm (110.24–114.17 in)
On M-EX Right Now
ASTM A681 P2
3 active listings and RFQs →
GB/T 1299 3Cr2W8V
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 P2 and GB/T 1299 3Cr2W8V?
ASTM A681 P2 specifies Mo, Ni which are not specified for GB/T 1299 3Cr2W8V. GB/T 1299 3Cr2W8V specifies W, V which are not specified for ASTM A681 P2.
Can ASTM A681 P2 be substituted with GB/T 1299 3Cr2W8V?
ASTM A681 P2 and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.