ASTM A681 P2 vs GOST 5950 3H2W8F

Minimal Match — 29.2% match based on chemical composition and mechanical property overlap.

ASTM A681 P2 (ASTM A681:2008) and GOST 5950 3H2W8F (GOST 5950-2000) are both steel grades. Both fall under the Tool & Die Steels category. ASTM A681 P2 is typically used for injection mould cavities, die casting dies for zinc, while GOST 5950 3H2W8F is commonly used for used for forging dies, extrusion tools, hot punches, mandrels, and die inserts.. ASTM A681 P2 is defined under ASTM International (United States).

As per chemical composition, ASTM A681 P2 vs GOST 5950 3H2W8F is a 43.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 29.2%.

Frequently Compared With ASTM A681 P2:
EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 EN ISO 683-17 100Cr6 GB/T 1299 3Cr2W8V GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS1 DIN EN ISO 4957 1.2344 GB/T 1299 4Cr5MoSiV GOST 5950 4H5MFS AISI 52100 IS 3748 103T3 IS 1570 (Part 6) 103T3
Match Breakdown
CHEMISTRY MATCH
43.8%
MECHANICAL MATCH
0%
OVERALL
29.2%
Specifications
Property ASTM A681 P2 GOST 5950 3H2W8F
Standard ASTM A681:2008 GOST 5950-2000
Category Tool & Die Steels Tool & Die Steels
C (%) <=0.10 0.3-0.4
Mn (%) 0.10-0.40 Not specified
P (%) <=0.030 Not specified
S (%) <=0.030 Not specified
Si (%) 0.10-0.40 0.2-0.5
Cr (%) 0.75-1.25 2.2-2.7
Mo (%) 0.15-0.40 Not specified
Ni (%) 0.10-0.50 Not specified
W (%) Not specified 7.5-9.0
V (%) Not specified 0.3-0.6
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A681 P2 GOST 5950 3H2W8F
Hardness <=100 HB 45-50 HRC
Condition Annealed (maximum Brinell hardness) Not specified
Tensile Strength Not specified 1400-1700 MPa
Yield Strength Not specified 1200 MPa min
Elongation Not specified 8% min
Typical Applications
ASTM A681 P2
Injection mould cavities, die casting dies for zinc
GOST 5950 3H2W8F
Used for forging dies, extrusion tools, hot punches, mandrels, and die inserts.
Key Differences
Can ASTM A681 P2 Be Substituted With GOST 5950 3H2W8F?
ASTM A681 P2 and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A681 P2
Round Bar → (3 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2700–3900 mm (106.3–153.54 in)
GOST 5950 3H2W8F
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–4300 mm (110.24–169.29 in)
On M-EX Right Now
ASTM A681 P2
3 active listings and RFQs →
GOST 5950 3H2W8F
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A681 P2 and GOST 5950 3H2W8F?
ASTM A681 P2 specifies Mn, P, S, Mo which are not specified for GOST 5950 3H2W8F. GOST 5950 3H2W8F specifies W, V which are not specified for ASTM A681 P2.
Can ASTM A681 P2 be substituted with GOST 5950 3H2W8F?
ASTM A681 P2 and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.