AS/NZS 1594 HA350 vs AS/NZS 3679.1 350

Strong Match — 98% match based on chemical composition and mechanical property overlap.

AS/NZS 1594 HA350 (AS/NZS 1594:2025) and AS/NZS 3679.1 350 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. AS/NZS 1594 HA350 is typically used for automotive structural parts, trailers, agricultural equipment, general fabrication, light structural sections., while AS/NZS 3679.1 350 is commonly used for hot-rolled structural bars and sections for primary structural beams, columns, and framing. AS/NZS 1594 HA350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand, while AS/NZS 3679.1 350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, AS/NZS 1594 HA350 vs AS/NZS 3679.1 350 is a 96.9% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 98%.

Frequently Compared With AS/NZS 1594 HA350:
AS/NZS 1595 C350 AS/NZS 1595 C450 IS 2062 E250B0 CSA G40.21 300W IS 2062 E250A AS/NZS 3679.1 300 ASTM A1008 SS Grade 80 ASTM A1008 SS Grade 50 CSA G40.21 400A ASTM A283C ASTM A572 Gr.65 ASTM A572 Grade 50
Match Breakdown
CHEMISTRY MATCH
96.9%
MECHANICAL MATCH
100%
OVERALL
98%
Specifications
Property AS/NZS 1594 HA350 AS/NZS 3679.1 350
Standard AS/NZS 1594:2025 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) max 0.2 <=0.22
Mn (%) max 1.6 <=1.70
Si (%) max 0.55 <=0.50
P (%) max 0.03 <=0.040
S (%) max 0.03 <=0.040
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AS/NZS 1594 HA350 AS/NZS 3679.1 350
Yield Strength 350 MPa min (AS/NZS 1594) 350 MPa min
Tensile Strength Not specified 480-640 MPa
Elongation Not specified 20% min
Typical Applications
AS/NZS 1594 HA350
Automotive structural parts, trailers, agricultural equipment, general fabrication, light structural sections.
AS/NZS 3679.1 350
Hot-rolled structural bars and sections for primary structural beams, columns, and framing
Can AS/NZS 1594 HA350 Be Substituted With AS/NZS 3679.1 350?
AS/NZS 1594 HA350 and AS/NZS 3679.1 350 overlap closely enough on chemistry and mechanical properties that AS/NZS 3679.1 350 is often considered as a substitute for AS/NZS 1594 HA350 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
AS/NZS 1594 HA350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3100–3600 mm (122.05–141.73 in)
AS/NZS 3679.1 350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3200 mm (114.17–125.98 in)
On M-EX Right Now
AS/NZS 1594 HA350
2 active listings and RFQs →
AS/NZS 3679.1 350
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between AS/NZS 1594 HA350 and AS/NZS 3679.1 350?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can AS/NZS 1594 HA350 be substituted with AS/NZS 3679.1 350?
AS/NZS 1594 HA350 and AS/NZS 3679.1 350 overlap closely enough on chemistry and mechanical properties that AS/NZS 3679.1 350 is often considered as a substitute for AS/NZS 1594 HA350 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.