Close Alternative — 82.3% match based on chemical composition and mechanical property overlap.

ASTM A105 (ASTM A105) and SAE J403 1002 (SAE J403:2009) are both steel grades. Both fall under the Carbon Steel category. ASTM A105 is typically used for flanges, fittings, valves, pressure piping components, forged pressure vessel parts, while SAE J403 1002 is commonly used for chemistry-only grade; product scope as listed in the composition notes. ASTM A105 is defined under ASTM International, originating from United States, while SAE J403 1002 is defined under SAE International, originating from United States.

As per chemical composition, ASTM A105 vs SAE J403 1002 is a 82.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.3%.

Frequently Compared With ASTM A105:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
82.3%
MECHANICAL MATCH
No shared data
OVERALL
82.3%
Specifications
Property ASTM A105 SAE J403 1002
Standard ASTM A105 SAE J403:2009
Category Carbon Steel Carbon Steel
C (%) ≤0.35 0.02-0.04
Mn (%) 0.60–1.05 <=0.35
Si (%) 0.10–0.35 Not specified
P (%) ≤0.035 <=0.030
S (%) ≤0.040 <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A105 SAE J403 1002
Tensile Strength 485 MPa min Not specified
Yield Strength 250 MPa min Not specified
Elongation ≥22% Not specified
Hardness ≤197 HB Not specified
Typical Applications
ASTM A105
Flanges, fittings, valves, pressure piping components, forged pressure vessel parts
SAE J403 1002
Chemistry-only grade; product scope as listed in the composition notes
Key Differences
Can ASTM A105 Be Substituted With SAE J403 1002?
ASTM A105 and SAE J403 1002 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
ASTM A105
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 6100–7000 mm (240.16–275.59 in)
SAE J403 1002
No active listings currently.
On M-EX Right Now
ASTM A105
2 active listings and RFQs →
SAE J403 1002
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A105 and SAE J403 1002?
ASTM A105 specifies Si which is not specified for SAE J403 1002.
Can ASTM A105 be substituted with SAE J403 1002?
ASTM A105 and SAE J403 1002 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.