ASTM A240/A240M S32808 vs ASTM A959 S39274

Related Material — 63.8% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S32808 (ASTM A240/A240M:2025) and ASTM A959 S39274 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S32808 is typically used for pressure vessels and general applications (plate, sheet and strip), while ASTM A959 S39274 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A240/A240M S32808 is defined under ASTM International, originating from United States, while ASTM A959 S39274 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A240/A240M S32808 vs ASTM A959 S39274 is a 63.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 63.8%.

Frequently Compared With ASTM A240/A240M S32808:
IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
63.8%
MECHANICAL MATCH
No shared data
OVERALL
63.8%
Specifications
Property ASTM A240/A240M S32808 ASTM A959 S39274
Standard ASTM A240/A240M:2025 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) <=1.10 <=1.00
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.020
Si (%) <=0.50 <=0.80
Cr (%) 27.0-27.9 24.0-26.0
Ni (%) 7.0-8.2 6.0-8.0
Mo (%) 0.80-1.2 2.5-3.5
N (%) 0.30-0.40 0.24-0.32
W (%) 2.10-2.50 1.50-2.50
Cu (%) Not specified 0.20-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S32808 ASTM A959 S39274
Tensile Strength >=700 MPa Not specified
Yield Strength >=500 MPa Not specified
Elongation >=15% Not specified
Hardness <=310 HB Not specified
Condition Plate, sheet and strip; yield by 0.2 percent offset Not specified
Typical Applications
ASTM A240/A240M S32808
Pressure vessels and general applications (plate, sheet and strip)
ASTM A959 S39274
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A240/A240M S32808 Be Substituted With ASTM A959 S39274?
ASTM A240/A240M S32808 and ASTM A959 S39274 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A240/A240M S32808
0 active listings and RFQs →
ASTM A959 S39274
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S32808 and ASTM A959 S39274?
ASTM A959 S39274 specifies Cu which is not specified for ASTM A240/A240M S32808.
Can ASTM A240/A240M S32808 be substituted with ASTM A959 S39274?
ASTM A240/A240M S32808 and ASTM A959 S39274 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.