ASTM A240/A240M:2025 S32906: S32906: duplex (austenitic-ferritic) stainless steel plate, sheet and strip (UNS number, no type name printed). Specified in ASTM A240/A240M:2025.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
Si
Cr
Ni
Mo
N
Cu
<=0.030
0.80-1.50
<=0.030
<=0.030
<=0.80
28.0-30.0
5.8-7.5
1.50-2.60
0.30-0.40
<=0.80
Mechanical Properties
Tensile Strength
>=800 MPa
Yield Strength
>=650 MPa
Elongation
>=25%
Hardness
<=310 HB
Condition
t < 0.4 in. [10.0 mm] (first condition printed); yield by 0.2 percent offset
More data from ASTM A240/A240M:2025
From the standard
Mechanical properties2 condition(s)
Product or thickness
Tensile strength, min (MPa)
Yield strength, min (MPa)
Elongation in 50 mm, min (%)
t < 0.4 in. [10.0 mm]
800
650
25.0
t >= 0.4 in. [10.0 mm]
750
550
25.0
Minimum values; yield strength by the 0.2 percent offset method.
Source: ASTM A240/A240M:2025, Table 2
Hardness2 condition(s)
Product or thickness
Brinell HBW, max
Rockwell, max
t < 0.4 in. [10.0 mm]
310
32 HRC
t >= 0.4 in. [10.0 mm]
310
32 HRC
Maximum values; either Brinell or Rockwell scale may be used.
Source: ASTM A240/A240M:2025, Table 2
Cold bend1 value
Cold bend angle
not required
Bend tests are not required for chromium steels thicker than 1 in. [25 mm] or for any austenitic or duplex steel regardless of thickness.
Source: ASTM A240/A240M:2025, Table 2