ASTM A240/A240M S32906 vs EN 10088-2 X2CrNiMoN29-7-2

Close Alternative — 75.5% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S32906 (ASTM A240/A240M:2025) and EN 10088-2 X2CrNiMoN29-7-2 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S32906 is typically used for pressure vessels and general applications (plate, sheet and strip), while EN 10088-2 X2CrNiMoN29-7-2 is commonly used for general purposes, hot or cold rolled sheet/plate and strip. ASTM A240/A240M S32906 is defined under ASTM International, originating from United States, while EN 10088-2 X2CrNiMoN29-7-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A240/A240M S32906 vs EN 10088-2 X2CrNiMoN29-7-2 is a 96.5% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a close alternative overall at 75.5%.

Frequently Compared With ASTM A240/A240M S32906:
EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
96.5%
MECHANICAL MATCH
33.3%
OVERALL
75.5%
Specifications
Property ASTM A240/A240M S32906 EN 10088-2 X2CrNiMoN29-7-2
Standard ASTM A240/A240M:2025 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Mn (%) 0.80-1.50 0.80-1.50
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.015
Si (%) <=0.80 <=0.50
Cr (%) 28.0-30.0 28.0-30.0
Ni (%) 5.8-7.5 5.8-7.5
Mo (%) 1.50-2.60 1.50-2.60
N (%) 0.30-0.40 0.30-0.40
Cu (%) <=0.80 <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S32906 EN 10088-2 X2CrNiMoN29-7-2
Tensile Strength >=800 MPa 800-1050 MPa
Yield Strength >=650 MPa >=650 MPa
Elongation >=25% >=20%
Hardness <=310 HB Not specified
Condition t < 0.4 in. [10.0 mm] (first condition printed); yield by 0.2 percent offset Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Typical Applications
ASTM A240/A240M S32906
Pressure vessels and general applications (plate, sheet and strip)
EN 10088-2 X2CrNiMoN29-7-2
General purposes, hot or cold rolled sheet/plate and strip
Can ASTM A240/A240M S32906 Be Substituted With EN 10088-2 X2CrNiMoN29-7-2?
ASTM A240/A240M S32906 and EN 10088-2 X2CrNiMoN29-7-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A240/A240M S32906
0 active listings and RFQs →
EN 10088-2 X2CrNiMoN29-7-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S32906 and EN 10088-2 X2CrNiMoN29-7-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A240/A240M S32906 be substituted with EN 10088-2 X2CrNiMoN29-7-2?
ASTM A240/A240M S32906 and EN 10088-2 X2CrNiMoN29-7-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.