ASTM A240/A240M S33425 vs IS 1570 (Part 5) X04Cr17Ni12Mo2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A240/A240M S33425 (ASTM A240/A240M:2025) and IS 1570 (Part 5) X04Cr17Ni12Mo2 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A240/A240M S33425 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A240/A240M S33425 vs IS 1570 (Part 5) X04Cr17Ni12Mo2 is a 72.7% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A240/A240M S33425:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
72.7%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property ASTM A240/A240M S33425 IS 1570 (Part 5) X04Cr17Ni12Mo2
Standard ASTM A240/A240M:2025 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Mn (%) <=1.50 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.020 <=0.030
Si (%) <=1.00 <=1.0
Cr (%) 21.0-23.0 16.0-18.0
Ni (%) 20.0-23.0 10.0-14.0
Mo (%) 2.00-3.00 2.0-3.0
Al (%) 0.15-0.60 Not specified
Ti (%) 0.15-0.60 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A240/A240M S33425 IS 1570 (Part 5) X04Cr17Ni12Mo2
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa >=205 MPa (0.2 % proof stress)
Elongation >=40% >=40% (50 mm)
Condition Plate, sheet and strip; yield by 0.2 percent offset Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Hardness Not specified <=217 HB; <=95 HRB
Typical Applications
ASTM A240/A240M S33425
Pressure vessels and general applications (plate, sheet and strip)
IS 1570 (Part 5) X04Cr17Ni12Mo2
Not documented
Key Differences
Can ASTM A240/A240M S33425 Be Substituted With IS 1570 (Part 5) X04Cr17Ni12Mo2?
ASTM A240/A240M S33425 and IS 1570 (Part 5) X04Cr17Ni12Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A240/A240M S33425
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr17Ni12Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A240/A240M S33425 and IS 1570 (Part 5) X04Cr17Ni12Mo2?
ASTM A240/A240M S33425 specifies Al, Ti which are not specified for IS 1570 (Part 5) X04Cr17Ni12Mo2.
Can ASTM A240/A240M S33425 be substituted with IS 1570 (Part 5) X04Cr17Ni12Mo2?
ASTM A240/A240M S33425 and IS 1570 (Part 5) X04Cr17Ni12Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.